PA6 PFL36沙伯基礎(chǔ)創(chuàng)新LNP™ LUBRICOMP™ PFL36 compound含玻纖PTFE（18024445500）

General Information
Product Description
LNP LUBRICOMP PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.

Also known as: LNP* LUBRICOMP* Compound PFL-4036
Product reorder name: PFL36
General　
Material Status　Commercial: Active

Availability　Asia Pacific

Filler / Reinforcement　Glass Fiber

Additive　PTFE Lubricant

Features　Lubricated

Processing Method　Injection Molding


ASTM & ISO Properties 1
Physical Nominal Value Unit Test Method
Density 1.51 g/cm³ ISO 1183
Mechanical Nominal Value Unit Test Method
Tensile Modulus 2 1.20E+6 psi ASTM D638
Tensile Modulus 1.14E+6 psi ISO 527-2/1
Tensile Strength (Yield) 16000 psi ASTM D638
Tensile Stress (Yield) 16400 psi ISO 527-2
Tensile Strength (Break) 15900 psi ASTM D638
Tensile Stress (Break) 16400 psi ISO 527-2
Tensile Elongation (Yield) 5.8 % ASTM D638
Tensile Strain (Yield) 4.1 % ISO 527-2
Tensile Elongation (Break) 6.7 % ASTM D638
Tensile Strain (Break) 4.5 % ISO 527-2
Flexural Modulus 800000 psi ASTM D790
Flexural Modulus 1.02E+6 psi ISO 178
Flexural Stress 24900 psi ISO 178
Impact Nominal Value Unit Test Method
Notched Izod Impact (73°F) 2.8 ft·lb/in ASTM D256
Notched Izod Impact Strength 3 (73°F) 7.9 ft·lb/in² ISO 180/1A
Unnotched Izod Impact (73°F) 20 ft·lb/in ASTM D4812
Unnotched Izod Impact Strength 3 (73°F) 38 ft·lb/in² ISO 180/1U
Instrumented Dart Impact (73°F, Energy at Peak Load) 168 in·lb ASTM D3763
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load (66 psi, Unannealed, 0.126 in) 421 °F ASTM D648
Heat Deflection Temperature 4 (66 psi, Unannealed, 2.52 in Span) 421 °F ISO 75-2/Bf
Deflection Temperature Under Load (264 psi, Unannealed, 0.126 in) 394 °F ASTM D648
Heat Deflection Temperature 4 (264 psi, Unannealed, 2.52 in Span) 396 °F ISO 75-2/Af

Processing Information
Injection Nominal Value Unit　
Drying Temperature 180 °F　
Drying Time 4.0 hr　
Suggested Max Moisture 0.15 to 0.25 %　
Rear Temperature 480 to 500 °F　
Middle Temperature 510 to 530 °F　
Front Temperature 530 to 550 °F　
Processing (Melt) Temp 510 to 530 °F　
Mold Temperature 180 to 200 °F　
Back Pressure 50.0 to 99.9 psi　
Screw Speed 30 to 60 rpm　

Notes
1Typical properties: these are not to be construed as specifications.
22.0 in/min
380*10*4
480*10*4 mm