PA66 AKV 35 H3.0 000000德國朗盛Durethan 35%玻纖熱老化穩定尼龍66塑料（18024445500）

PA 66, 35 % glass fibers, injection molding, heat-aging stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 66, GHR, 14-110, GF35

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 0.37　
C Molding shrinkage, transverse 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 1.06　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11200 7500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 200 135
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1　7000
C Tensile creep modulus 1000 h MPa ISO 899-1　5800
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 85 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 12 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 80　
Izod impact strength -30 °C kJ/m² ISO 180-1U 70　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 12 15
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 10500 7000
Flexural strength 2 mm/min MPa ISO 178-A 300 220
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0